DIN1629 St35.8 Agbara to gaju 42CrMo 12Cr1MoVG 40Cr Pipe Irin Alailowaya fun Ohun elo igbomikana Titẹ giga

Lati ṣẹda anfani pupọ diẹ sii fun awọn onijaja ni imoye ile-iṣẹ wa;client grow is our working chase for DIN1629 St35.8 High Pressure 42CrMo 12Cr1MoVG 40Cr Seamless Steel Pipe for High Pressure Boiler Material, A, pẹlu itara nla ati otitọ, ni o fẹ lati pese fun ọ pẹlu awọn iṣẹ pipe ati lilọsiwaju pẹlu rẹ lati ṣẹda imọlẹ kan. ojo iwaju.
Lati ṣẹda anfani pupọ diẹ sii fun awọn onijaja ni imoye ile-iṣẹ wa;ni ose dagba ni wa ṣiṣẹ Chase funChina 42CrMo 40Cr Alailẹgbẹ Irin Pipe, Fun ẹnikẹni ti o ni itara lori eyikeyi awọn ohun wa ni kete lẹhin ti o wo atokọ ọja wa, o yẹ ki o ni idaniloju ni ominira lati ni ifọwọkan pẹlu wa fun awọn ibeere.O ni anfani lati firanṣẹ awọn imeeli wa ki o kan si wa fun ijumọsọrọ ati pe a yoo dahun si ọ ni kete bi a ti le.Ti o ba rọrun, o le wa adirẹsi wa ni oju opo wẹẹbu wa ki o wa si iṣowo wa fun alaye diẹ sii ti ọjà wa nipasẹ tirẹ.A n ṣetan nigbagbogbo lati kọ awọn ibatan ifowosowopo ti o gbooro ati iduroṣinṣin pẹlu eyikeyi awọn alabara ti o ṣeeṣe ni awọn aaye ti o jọmọ.

O ni ko si kedere ibinu brittleness, kekere abuku nigba quenching, ga rirẹ iye to ati ọpọ ikolu resistance lẹhin quenching ati tempering itọju.42CrMo alloy pipe pipe ni ipa lile ti o dara ni iwọn otutu kekere ati agbara ti nrakò ati agbara ifarada ni iwọn otutu giga.Dada quenching lẹhin quenching ati tempering ti wa ni maa lo bi awọn ooru itọju eni fun 42CrMo alloy seamless oniho.

Alloy pataki irin: 41Cr4,25CrMo4,30CrMo4,34CrMo4,42CrMo4

OD: 20-660mm WT: 2.3-100mm L: 5.8M, 6M, 11.8M, 12M tabi eyikeyi miiran pato ipari.

Ohun elo: Ṣiṣe ẹrọ, Imọ-ẹrọ gbogbogbo, apa Kireni, Bushes, Awọn Cylinders Orisirisi, Awọn Rolls Conveyor, Awọn ọpa ṣofo, Awọn apakan ṣofo ati awọn paati, Awọn eso, Awọn oruka, bbl

Ohun elo 42CrMo alloy pipe pipe: irin pataki ti a lo fun awọn afara jẹ “42CrMo”, irin pataki fun awọn girders ọkọ ayọkẹlẹ jẹ “42CrMo”, ati irin pataki fun awọn ohun elo titẹ jẹ “42CrMo”.Iru irin yii ṣe ilọsiwaju awọn ohun-ini ẹrọ ti irin nipasẹ ṣiṣatunṣe akoonu erogba (c).Nitorinaa, ni ibamu si akoonu erogba, iru irin yii le pin si: irin kekere erogba - akoonu erogba ni gbogbogbo kere ju 0.25%, bii 10 ati 20 irin;Irin erogba alabọde - akoonu erogba ni gbogbogbo laarin 0.25 ati 0.60%, bii 35 ati 45 irin;Irin erogba giga - akoonu erogba ni gbogbogbo tobi ju 0.60%.Iru irin yii kii ṣe lo lati ṣe awọn paipu irin.

Ohun elo Aṣoju
Dara fun ṣiṣe awọn apẹrẹ ṣiṣu nla ati alabọde ti o nilo agbara kan ati lile.

Awọn ifarada ti Awọn Gigun:
Nigbati Gigun ba dọgba si 6000mm, Awọn ifarada 0/+10
Nigbati 6 000 <L = 12 000, Awọn ifarada 0/+15
Nigbati> 12 000, Awọn ifarada 0/+ nipasẹ adehun
Sipesifikesonu ilana ati awọn ohun-ini ti ara ti paipu irin 42CrMo
42CrMo irin pipe, erogba akoonu: 0.38 ~ 0.45%, silikoni: 0.17 ~ 0.37%, manganese: 0.50 ~ 0.80%.

Paipu irin 42CrMo jẹ ti irin alagbara giga-giga, pẹlu agbara giga ati lile, lile ti o dara, ko si brittleness tempering ti o han gbangba, opin rirẹ giga ati resistance ipa pupọ lẹhin quenching ati itọju tempering, ati ipa lile iwọn otutu kekere ti o dara.

Irin naa dara fun iṣelọpọ awọn apẹrẹ ṣiṣu nla ati alabọde ti o nilo agbara kan ati lile.Aami ami agbari boṣewa kariaye ti o baamu: 42CrMo4 ni ibamu si ami iyasọtọ Japanese: scm440 ni ibamu si ami iyasọtọ German: 42CrMo4 isunmọ ni ibamu si ami iyasọtọ Amẹrika: awọn abuda 4140 ati ipari ohun elo: agbara giga, hardenability, toughness ti o dara, abuku kekere lakoko piparẹ, agbara ti nrakò ati agbara ifarada ni iwọn otutu giga.O ti wa ni lo lati lọpọ forgings pẹlu ti o ga agbara ati ki o tobi quenching ati tempering agbelebu-apakan ju 35CrMo, irin, gẹgẹ bi awọn ti o tobi jia fun locomotive isunki, gbigbe jia ti supercharger, ru axle, asopọ opa ati orisun omi dimole pẹlu nla fifuye, lu paipu isẹpo ati ọpa ipeja fun epo jinle daradara ni isalẹ 2000m, ati mimu fun ẹrọ atunse.

Sulfur s: akoonu iyokù ti a gba laaye ≤ 0.035%

Phosphorus P: akoonu ti o ku laaye ≤ 0.035%

Chromium (CR): 0.90 ~ 1.20%

Nickel Ni: akoonu ti o ku laaye ≤ 0.030%

Copper Cu: akoonu ti o ku laaye ≤ 0.030%

Molybdenum (MO): 0.15 ~ 0.25%

Allowable wahala ti 42CrMo

42CrMo Allowable wahala 186 ~ 310 / MPa, ikore ojuami 930 σ S / MPa, 42CrMo ni o ni ga agbara, hardenability, ti o dara toughness, kekere abuku nigba quenching, ati ki o ga ti nrakò agbara ati ìfaradà agbara ni ga otutu.42CrMo paipu irin ti wa ni lilo lati ṣe awọn forgings pẹlu agbara ti o ga ati ki o tobi parun ati tempered apakan ju 35CrMo irin.

1) Lominu iwọn otutu (isunmọ): AC1 = 730 ° C, AC3 = 800 ° C, Ms = 310 ° C.

2) Olusọdipúpọ imugboroja laini: iwọn otutu 20 ~ 100 ° C / 20 ~ 200 ° C / 20 ~ 300 ° C / 20 ~ 400 ° C / 20 ~ 500 ° C / 20 ~ 600 ° C, olùsọdipúpọ imugboroja laini: 11.1 × 10K /12.1 × 10K/12.9 × 10K/13.5 × 10K/13.9 × 10K14.1 × 10K.

3) Iwọn rirọ: iwọn otutu 20 ° C / 300 ° C / 400 ° C / 500 ° C / 600 ° C, rirọ modulus 210000mpa / 185000mpa / 175000mpa / 165000mpa / 15500mpa

Gbona ṣiṣẹ sipesifikesonu
Iwọn otutu alapapo jẹ 1150 ~ 1200 ° C, iwọn otutu ibẹrẹ jẹ 1130 ~ 1180 ° C, ati iwọn otutu ipari jẹ> 850 ° C, φ> 50mm, itutu agbaiye lọra.

Normalizing sipesifikesonu
Iwọn otutu deede jẹ 850 ~ 900 ° C, ati ileru ti tutu nipasẹ afẹfẹ.

Ga otutu tempering sipesifikesonu
Awọn iwọn otutu otutu jẹ 680 ~ 700 ° C, ati ileru ti wa ni tutu nipasẹ afẹfẹ.

Quenching ati tempering ni pato
Preheating otutu 680 ~ 700 ° C, quenching otutu 840 ~ 880 ° C, epo itutu, tempering otutu 580 ° C, omi itutu tabi epo itutu, líle ≤ 217hbw.

Sipesifikesonu fun subcritical okun ati toughening
Pipa otutu 900 ° C, otutu otutu 560 ° C, lile (37 ± 1) HRC

Sipesifikesonu fun fifa irọbi quenching ati tempering
Quenching otutu 900 ° C, tempering otutu 150 ~ 180 ° C, líle 54 ~ 60HRC.

Gbona ṣiṣẹ sipesifikesonu
Iwọn otutu alapapo jẹ 1150 ~ 1200 ° C, iwọn otutu ibẹrẹ jẹ 1130 ~ 1180 ° C, ati iwọn otutu ipari jẹ> 850 ° C, φ> 50mm, itutu agbaiye lọra.

Normalizing sipesifikesonu
Iwọn otutu deede jẹ 850 ~ 900 ° C, ati ileru ti tutu nipasẹ afẹfẹ.

Ga otutu tempering sipesifikesonu
Awọn iwọn otutu otutu jẹ 680 ~ 700 ° C, ati ileru ti wa ni tutu nipasẹ afẹfẹ.

Quenching ati tempering ni pato
Preheating otutu 680 ~ 700 ° C, quenching otutu 840 ~ 880 ° C, epo itutu, tempering otutu 580 ° C, omi itutu tabi epo itutu, líle ≤ 217hbw.

Sipesifikesonu fun subcritical okun ati toughening
Pipa otutu 900 ° C, otutu otutu 560 ° C, lile (37 ± 1) HRC

Sipesifikesonu fun fifa irọbi quenching ati tempering
Quenching otutu 900 ° C, tempering otutu 150 ~ 180 ° C, líle 54 ~ 60HRC.

Lati ṣẹda anfani pupọ diẹ sii fun awọn onijaja ni imoye ile-iṣẹ wa;ibaramu ti n dagba ni ilepa iṣẹ wa fun Didara to dara DIN1629 St35.8 Agbara Agbara Erogba Irin Alailẹgbẹ Pipe 12cr1movg 42CrMo 40cr Pipe Irin Pipe fun Ohun elo Boiler Agbara giga , A, pẹlu itara nla ati otitọ, ni o ṣetan lati pese fun ọ pẹlu awọn iṣẹ pipe ati lilọsiwaju siwaju pẹlu rẹ lati ṣẹda kan imọlẹ ojo iwaju.
Didara Didara China Irin Pipe ati Ọpọn Irin, Fun ẹnikẹni ti o ni itara lori eyikeyi awọn ohun wa lẹsẹkẹsẹ lẹhin ti o wo atokọ ọja wa, o yẹ ki o ni idaniloju ni ominira lati ni ifọwọkan pẹlu wa fun awọn ibeere.O ni anfani lati firanṣẹ awọn imeeli wa ki o kan si wa fun ijumọsọrọ ati pe a yoo dahun si ọ ni kete bi a ti le.Ti o ba rọrun, o le wa adirẹsi wa ni oju opo wẹẹbu wa ki o wa si iṣowo wa fun alaye diẹ sii ti ọjà wa nipasẹ tirẹ.A n ṣetan nigbagbogbo lati kọ awọn ibatan ifowosowopo ti o gbooro ati iduroṣinṣin pẹlu eyikeyi awọn alabara ti o ṣeeṣe ni awọn aaye ti o jọmọ.
f have any inquiry about 42CrMo alloy seamless steel pipe ,please kindly send me details to email:bruce@haihuisteel.com or 0086-15865769231(whatsapp),we would like to provide our best price as soon as possible.We also can provide steel pipe cutting service according to your demands.
Kaabo lati ṣabẹwo si ile-iṣẹ wa, nireti lati ni ifọwọsowọpọ pẹlu ile-iṣẹ ti o niyi!